The Influence of Hot Isostatic Pressing on the Mechanical Properties of Ti-6Al-4V Samples Printed Using the LENS Method

Bożena Gzik-Zroska; Kamil Joszko; Agata Piątek; Wojciech Wolański; Edyta Kawlewska; Arkadiusz Szarek; Wojciech Kajzer; Grzegorz Stradomski

doi:10.3390/ma18030612

The Influence of Hot Isostatic Pressing on the Mechanical Properties of Ti-6Al-4V Samples Printed Using the LENS Method

Bożena Gzik-Zroska
, Kamil Joszko
, Agata Piątek
, Wojciech Wolański
, Edyta Kawlewska
, Arkadiusz Szarek
, Wojciech Kajzer
, Grzegorz Stradomski

Silesian University of Technology
Częstochowa University of Technology

Wyniki badań: Wkład do czasopisma › Artykuł › recenzja

2 Cytowania z bazy Scopus

Abstrakt

The aim of this work was to assess the influence of the parameters of the hot isostatic pressing (HIP) process and the direction of printing of Ti-6Al-4V samples made using the laser-engineered net shaping (LENS) method on strength properties. The tests were carried out using a static testing machine and a digital image correlation system. Samples before and after the HIP process were tested. The HIP process was carried out at a temperature of 1150 °C, a heating time of 240 min and various pressure values of 500, 1000 and 1500 bar. Based on the comparative analysis of the test results, it has been shown that the ability to adjust the parameters of the HIP process has a significant impact on the final mechanical properties of the samples.

Język oryginału	angielski
Numer artykułu	612
Czasopismo	Materials
Tom	18
Numer wydania	3
Identyfikatory DOI	https://doi.org/10.3390/ma18030612
Status publikacji	Opublikowano - lut 2025

Obszary tematyczne ASJC Scopus

Materiałoznawstwo ogólne
Fizyka materii skondensowanej

Uzyskaj dostęp do dokumentu

10.3390/ma18030612

Inne pliki i linki

Link do publikacji w Scopus

Cytowanie

@article{94992d52548e43a79418dd3fc9ef9588,

title = "The Influence of Hot Isostatic Pressing on the Mechanical Properties of Ti-6Al-4V Samples Printed Using the LENS Method",

abstract = "The aim of this work was to assess the influence of the parameters of the hot isostatic pressing (HIP) process and the direction of printing of Ti-6Al-4V samples made using the laser-engineered net shaping (LENS) method on strength properties. The tests were carried out using a static testing machine and a digital image correlation system. Samples before and after the HIP process were tested. The HIP process was carried out at a temperature of 1150 °C, a heating time of 240 min and various pressure values of 500, 1000 and 1500 bar. Based on the comparative analysis of the test results, it has been shown that the ability to adjust the parameters of the HIP process has a significant impact on the final mechanical properties of the samples.",

keywords = "3D printing parameters, digital image correlation, static tensile test, titanium alloy",

author = "Bo{\.z}ena Gzik-Zroska and Kamil Joszko and Agata Pi{\c a}tek and Wojciech Wola{\'n}ski and Edyta Kawlewska and Arkadiusz Szarek and Wojciech Kajzer and Grzegorz Stradomski",

note = "Publisher Copyright: {\textcopyright} 2025 by the authors.",

year = "2025",

month = feb,

doi = "10.3390/ma18030612",

language = "English",

volume = "18",

journal = "Materials",

issn = "1996-1944",

publisher = "Multidisciplinary Digital Publishing Institute (MDPI)",

number = "3",

}

TY - JOUR

T1 - The Influence of Hot Isostatic Pressing on the Mechanical Properties of Ti-6Al-4V Samples Printed Using the LENS Method

AU - Gzik-Zroska, Bożena

AU - Joszko, Kamil

AU - Piątek, Agata

AU - Wolański, Wojciech

AU - Kawlewska, Edyta

AU - Szarek, Arkadiusz

AU - Kajzer, Wojciech

AU - Stradomski, Grzegorz

PY - 2025/2

Y1 - 2025/2

N2 - The aim of this work was to assess the influence of the parameters of the hot isostatic pressing (HIP) process and the direction of printing of Ti-6Al-4V samples made using the laser-engineered net shaping (LENS) method on strength properties. The tests were carried out using a static testing machine and a digital image correlation system. Samples before and after the HIP process were tested. The HIP process was carried out at a temperature of 1150 °C, a heating time of 240 min and various pressure values of 500, 1000 and 1500 bar. Based on the comparative analysis of the test results, it has been shown that the ability to adjust the parameters of the HIP process has a significant impact on the final mechanical properties of the samples.

AB - The aim of this work was to assess the influence of the parameters of the hot isostatic pressing (HIP) process and the direction of printing of Ti-6Al-4V samples made using the laser-engineered net shaping (LENS) method on strength properties. The tests were carried out using a static testing machine and a digital image correlation system. Samples before and after the HIP process were tested. The HIP process was carried out at a temperature of 1150 °C, a heating time of 240 min and various pressure values of 500, 1000 and 1500 bar. Based on the comparative analysis of the test results, it has been shown that the ability to adjust the parameters of the HIP process has a significant impact on the final mechanical properties of the samples.

KW - 3D printing parameters

KW - digital image correlation

KW - static tensile test

KW - titanium alloy

UR - https://www.scopus.com/pages/publications/85217756199

U2 - 10.3390/ma18030612

DO - 10.3390/ma18030612

M3 - Article

AN - SCOPUS:85217756199

SN - 1996-1944

VL - 18

JO - Materials

JF - Materials

IS - 3

M1 - 612

ER -

The Influence of Hot Isostatic Pressing on the Mechanical Properties of Ti-6Al-4V Samples Printed Using the LENS Method

Abstrakt

Obszary tematyczne ASJC Scopus

Uzyskaj dostęp do dokumentu

Inne pliki i linki

Fingerprint

Cytowanie