Selection of parameters of the manufacturing process of composites AlMMC / CF by GPI - Composition of matrix alloy

M. Dyzia; A. J. Dolata; J. Śleziona

Selection of parameters of the manufacturing process of composites AlMMC / C_F by GPI - Composition of matrix alloy

M. Dyzia
, A. J. Dolata
, J. Śleziona

Katedra Technologii Materiałowych (RM/RM3)

Silesian University of Technology

Wyniki badań: Rozdział w książce/raport/materiał konferencyjny › Wkład w konferencję › recenzja

Abstrakt

Obtaining a strong bonding on the carbon fiber and aluminium matrix interface, require a favorable wetting conditions and limitations reactivity between the aluminium matrix and carbon fibres. In the processes of infiltration, one of the factors conducive to such a connection is the chemical composition of the alloy matrix. The composition of the alloy also decides on technological properties such as castability and shrinkage. The paper presents the results of comparative fluidity tests of AlSi9Cu(Fe) and AlSi9Mn alloy with addition of magnesium and strontium. It was compared the metal flow path in the beam with a width of 20 mm and different thicknesses in the graphite mould. In case of modified alloy AlSi9Cu(Fe) + 1% Mg +0.03%Sr was observed a slight decrease of fluidity. While in the case of alloy AlSi9Mn+ 1% Mg +0.03%Sr length of filled increased comparing to similar beams on base alloy.

Język oryginału	angielski
Tytuł publikacji goszczącej	ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials
Wydawca	European Conference on Composite Materials, ECCM
ISBN (drukowany)	9788888785332
Status publikacji	Opublikowano - 2012
Wydarzenie	15th European Conference on Composite Materials: Composites at Venice, ECCM 2012 - Venice, Włochy Czas trwania: 24 cze 2012 → 28 cze 2012

Seria publikacji

Nazwa	ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials

Konferencja

Konferencja	15th European Conference on Composite Materials: Composites at Venice, ECCM 2012
Kraj/Terytorium	Włochy
Miejscowość	Venice
Okres	24/06/12 → 28/06/12

Cele SDG ONZ

Ten wynik przyczynia się do realizacji następujących celów zrównoważonego rozwoju

Cel 9 Przemysł, innowacje i infrastruktura

Obszary tematyczne ASJC Scopus

Ceramika i kompozyty

Inne pliki i linki

Link do publikacji w Scopus

Cytowanie

Dyzia, M., Dolata, A. J., & Śleziona, J. (2012). Selection of parameters of the manufacturing process of composites AlMMC / C_F by GPI - Composition of matrix alloy. W ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials (ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials). European Conference on Composite Materials, ECCM.

Dyzia, M. ; Dolata, A. J. ; Śleziona, J. / Selection of parameters of the manufacturing process of composites AlMMC / C_F by GPI - Composition of matrix alloy. ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials. European Conference on Composite Materials, ECCM, 2012. (ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials).

@inproceedings{6d807b318a67417397fd03e57df4b162,

title = "Selection of parameters of the manufacturing process of composites AlMMC / CF by GPI - Composition of matrix alloy",

abstract = "Obtaining a strong bonding on the carbon fiber and aluminium matrix interface, require a favorable wetting conditions and limitations reactivity between the aluminium matrix and carbon fibres. In the processes of infiltration, one of the factors conducive to such a connection is the chemical composition of the alloy matrix. The composition of the alloy also decides on technological properties such as castability and shrinkage. The paper presents the results of comparative fluidity tests of AlSi9Cu(Fe) and AlSi9Mn alloy with addition of magnesium and strontium. It was compared the metal flow path in the beam with a width of 20 mm and different thicknesses in the graphite mould. In case of modified alloy AlSi9Cu(Fe) + 1\% Mg +0.03\%Sr was observed a slight decrease of fluidity. While in the case of alloy AlSi9Mn+ 1\% Mg +0.03\%Sr length of filled increased comparing to similar beams on base alloy.",

keywords = "Aluminium matrix composites (AlMMC), Carbon fibres, Modification of base alloy, Wettability",

author = "M. Dyzia and Dolata, \{A. J.\} and J. {\'S}leziona",

year = "2012",

language = "English",

isbn = "9788888785332",

series = "ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials",

publisher = "European Conference on Composite Materials, ECCM",

booktitle = "ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials",

note = "15th European Conference on Composite Materials: Composites at Venice, ECCM 2012 ; Conference date: 24-06-2012 Through 28-06-2012",

}

Dyzia, M , Dolata, AJ & Śleziona, J 2012, Selection of parameters of the manufacturing process of composites AlMMC / C_F by GPI - Composition of matrix alloy. w ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials. ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials, European Conference on Composite Materials, ECCM, 15th European Conference on Composite Materials: Composites at Venice, ECCM 2012, Venice, Włochy, 24/06/12.

Selection of parameters of the manufacturing process of composites AlMMC / C_F by GPI - Composition of matrix alloy. / Dyzia, M.; Dolata, A. J.; Śleziona, J.
ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials. European Conference on Composite Materials, ECCM, 2012. (ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials).

Wyniki badań: Rozdział w książce/raport/materiał konferencyjny › Wkład w konferencję › recenzja

TY - GEN

T1 - Selection of parameters of the manufacturing process of composites AlMMC / CF by GPI - Composition of matrix alloy

AU - Dyzia, M.

AU - Dolata, A. J.

AU - Śleziona, J.

PY - 2012

Y1 - 2012

N2 - Obtaining a strong bonding on the carbon fiber and aluminium matrix interface, require a favorable wetting conditions and limitations reactivity between the aluminium matrix and carbon fibres. In the processes of infiltration, one of the factors conducive to such a connection is the chemical composition of the alloy matrix. The composition of the alloy also decides on technological properties such as castability and shrinkage. The paper presents the results of comparative fluidity tests of AlSi9Cu(Fe) and AlSi9Mn alloy with addition of magnesium and strontium. It was compared the metal flow path in the beam with a width of 20 mm and different thicknesses in the graphite mould. In case of modified alloy AlSi9Cu(Fe) + 1% Mg +0.03%Sr was observed a slight decrease of fluidity. While in the case of alloy AlSi9Mn+ 1% Mg +0.03%Sr length of filled increased comparing to similar beams on base alloy.

AB - Obtaining a strong bonding on the carbon fiber and aluminium matrix interface, require a favorable wetting conditions and limitations reactivity between the aluminium matrix and carbon fibres. In the processes of infiltration, one of the factors conducive to such a connection is the chemical composition of the alloy matrix. The composition of the alloy also decides on technological properties such as castability and shrinkage. The paper presents the results of comparative fluidity tests of AlSi9Cu(Fe) and AlSi9Mn alloy with addition of magnesium and strontium. It was compared the metal flow path in the beam with a width of 20 mm and different thicknesses in the graphite mould. In case of modified alloy AlSi9Cu(Fe) + 1% Mg +0.03%Sr was observed a slight decrease of fluidity. While in the case of alloy AlSi9Mn+ 1% Mg +0.03%Sr length of filled increased comparing to similar beams on base alloy.

KW - Aluminium matrix composites (AlMMC)

KW - Carbon fibres

KW - Modification of base alloy

KW - Wettability

UR - https://www.scopus.com/pages/publications/84903973712

M3 - Conference contribution

AN - SCOPUS:84903973712

SN - 9788888785332

T3 - ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials

BT - ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials

PB - European Conference on Composite Materials, ECCM

T2 - 15th European Conference on Composite Materials: Composites at Venice, ECCM 2012

Y2 - 24 June 2012 through 28 June 2012

ER -

Dyzia M , Dolata AJ, Śleziona J. Selection of parameters of the manufacturing process of composites AlMMC / C_F by GPI - Composition of matrix alloy. W ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials. European Conference on Composite Materials, ECCM. 2012. (ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials).