Post-Processing Effect on the Corrosion Resistance of Super Duplex Stainless Steel Produced by Laser Powder Bed Fusion

This study examines the microstructural characteristics and corrosion resistance of super duplex stainless steel (SDSS) produced through laser powder bed fusion (LPBF). The analysis shows that the as-printed samples mainly exhibit a ferritic microstructure, which is due to the fast-cooling rates of the LPBF technique. X-ray and microstructure analyses reveal the presence of minor austenite phases in the ferritic matrix. The process of solution annealing led to a more balanced microstructure. Analyses of corrosion resistance, such as potentiodynamic polarization tests and EIS, indicate that heat treatment has a significant impact on the corrosion behavior of SDSS. Solution annealing and stress relieving at 400 °C for 1 h can improve corrosion resistance by increasing polarization resistance and favorable EIS parameters. However, stress relieving at 550 °C for 5 h may reduce the material’s corrosion resistance due to the formation of chromium nitride. Therefore, stress relieving at 400 °C for 1 h is a practical method to significantly enhance the corrosion resistance of LPBF-printed SDSS. This method offers a balance between microstructural integrity and material performance.