The influence of deposition process on structure of platinum-modifed aluminide coatings o Ni-base superalloy

The modern jet engines used in commercial and military aircrafts are characterized by operating temperature in turbine section above 1000°C. The Ni-base superalloy turbine blades and vanes working in high temperature in very aggressive environment require using of protective coatings. The aluminide coatings are widely used to protect this engine parts. The pack cementation, out of pack and chemical vapour deposition (CVD) technologies are usually used to produce this type of coating. The aluminide coatings can be modified by platinum or other elements. The Ptmodified aluminide coatings are characterized by better oxidation and corrosion resistance in comparison with conventional aluminide coatings and can be used as a bond coat for Thermal Barrier Coatings deposited by EB-PVD technology. In present study the influence of deposition technology and their's parameters on structure and chemical composition of Pt-aluminide coatings are presented. The base material for coatings was a Inconel 738 Ni-base superalloy. The first step of coatings production were Pt electroplating with different thickness of platinum layer. The second step of coating production was aluminising process. The aluminide coatings were produced by pack cementation and out of pack technologies. Additional the influence of heat treatment of base alloy with coatings was investigated. The structure of all deposited coatings was observed by scanning electron microscopy and the chemical and phase composition of coatings were investigated by EDS and XRD methods. The observed coatings were characterized by two types of structure: first based on NiAlPt phase obtained on thin Pt layer and the second with additional presence of PtAl₂ phase on the thick Pt layer.