Abstract
A photo-rheology method was applied to determine photochemical reactivity of poly(lactic acid) close to glass transition region. The differences in the rheological behaviour were measured during in situ UV irradiation in air. At low frequency (1 rad s-1), the highest reactivity was observed at the glass transition temperature which corresponds to the data from DSC. Below and above this temperature, the rate of PLA chain scission degradation was lower. Moreover, it was also shown that changing the oscillation frequency led to the maximal rate of the chain scission rate occurring at temperatures slightly higher (shifted due to time-temperature superposition effects).
| Original language | English |
|---|---|
| Pages (from-to) | 239-246 |
| Number of pages | 8 |
| Journal | European Polymer Journal |
| Volume | 81 |
| DOIs | |
| Publication status | Published - 1 Aug 2016 |
Keywords
- Glass transition region
- Photo-rheology
- Poly(lactic acid)
- UV irradiation
ASJC Scopus subject areas
- General Physics and Astronomy
- Polymers and Plastics
- Organic Chemistry
- Materials Chemistry
Fingerprint
Dive into the research topics of 'Photochemical reactivity of PLA at the vicinity of glass transition temperature. the photo-rheology method'. Together they form a unique fingerprint.Cite this
- APA
- Author
- BIBTEX
- Harvard
- Standard
- RIS
- Vancouver