T1 - Influence of solutionizing parameters on the structure and corrosion resistance of the ZnAl40Cu3 alloy
AU - Tomaszewska, Agnieszka
AU - Michalik, Rafał
AU - Jabłońska, Magdalena
N1 - Publisher Copyright:
© 2016 Trans Tech Publications.
PY - 2016
Y1 - 2016
N2 - The purpose of carried out examination was to determine the effect of solution heat treatment on the structure and corrosion resistance of the ZnAl40Cu3 alloy in the "acid rain" environment. The scope of the test included Brinell hardness tests, structural tests and galvanostatic and potentiodynamic tests. The examination showed that the maximum hardness of the sample after solution heat treatment obtain after 10 h of solutionizing. It has been shown that the solutionizing increases the corrosion resistance. The corrosion resistance was greater, when the longer was the time of solutionizing.
AB - The purpose of carried out examination was to determine the effect of solution heat treatment on the structure and corrosion resistance of the ZnAl40Cu3 alloy in the "acid rain" environment. The scope of the test included Brinell hardness tests, structural tests and galvanostatic and potentiodynamic tests. The examination showed that the maximum hardness of the sample after solution heat treatment obtain after 10 h of solutionizing. It has been shown that the solutionizing increases the corrosion resistance. The corrosion resistance was greater, when the longer was the time of solutionizing.
KW - Corrosion
KW - Heat treatment
KW - Structure
KW - Zn-Al-Cu alloys
UR - https://www.scopus.com/pages/publications/84959121408
U2 - 10.4028/www.scientific.net/SSP.246.123
DO - 10.4028/www.scientific.net/SSP.246.123
M3 - Conference contribution
AN - SCOPUS:84959121408
SN - 9783038355212
T3 - Solid State Phenomena
SP - 123
EP - 126
BT - Technologies and Properties of Modern Utility Materials XXIII
A2 - Szczotok, Agnieszka
A2 - Szkliniarz, Agnieszka
A2 - Mendala, Jacek
PB - Trans Tech Publications Ltd.
T2 - 23rd Conference on Technologies and Properties of Modern Utility Materials, TPMUM 2015
Y2 - 15 May 2015 through 15 May 2015
ER -