T1 - Heredity of the structure and properties of grey cast iron melted on a basis of steel scrap
AU - Janerka, Krzysztof
AU - Jezierski, Jan
AU - Bartocha, Dariusz
AU - Szajnar, Jan
PY - 2013
Y1 - 2013
N2 - In this paper are presented the results of researches, obtained during cast iron melting on basis of steel scrap and a carburizer (without pig iron in solid charge). In the process of carburization, there were used the carburizers such as anthracite, natural and synthetic graphite, petroleum and cupola coke, as well as charcoal. The grey cast iron was produced, for which quantitative analysis of graphite precipitations was performed. It was noticed that in case of using anthracite as carburizer, the smaller graphite precipitations were obtained. In authors' opinion they are consequences of anthracite structure, consisted of fine graphite flakes and phenomenon of charge materials features' transfer into melted alloys (structure heredity).
AB - In this paper are presented the results of researches, obtained during cast iron melting on basis of steel scrap and a carburizer (without pig iron in solid charge). In the process of carburization, there were used the carburizers such as anthracite, natural and synthetic graphite, petroleum and cupola coke, as well as charcoal. The grey cast iron was produced, for which quantitative analysis of graphite precipitations was performed. It was noticed that in case of using anthracite as carburizer, the smaller graphite precipitations were obtained. In authors' opinion they are consequences of anthracite structure, consisted of fine graphite flakes and phenomenon of charge materials features' transfer into melted alloys (structure heredity).
KW - Heredity of the structure
KW - Recarburization
KW - Synthetic cast iron
UR - https://www.scopus.com/pages/publications/84872736668
U2 - 10.4028/www.scientific.net/AMR.622-623.685
DO - 10.4028/www.scientific.net/AMR.622-623.685
M3 - Conference contribution
AN - SCOPUS:84872736668
SN - 9783037855638
T3 - Advanced Materials Research
SP - 685
EP - 689
BT - Manufacturing Science and Technology III
T2 - 2012 3rd International Conference on Manufacturing Science and Technology, ICMST 2012
Y2 - 18 August 2012 through 19 August 2012
ER -